- Effect of Chemical Structure on the Performance of Sulfonated Poly(aryl ether sulfone) Composite Nanofiltration Membranes
- 点击次数：
- 论文类型： 期刊论文
- 发表时间： 2019-01-01
- 发表刊物： MEMBRANES
- 收录刊物： PubMed、SCIE、EI
- 卷号： 9
- 期号： 1
- 关键字： sulfonated poly(aryl ether sulfone); phthalazinone; structure; composite membranes; nanofiltration
- 摘要： This paper discusses the effect of the chemical structure of sulfonated poly(aryl ether sulfone) on the performance of composite nanofiltration membranes. The composite nanofiltration membranes were fabricated by coating sulfonated poly(aryl ether sulfone) solution onto the top surface of poly(phthalazinone ether sulfone ketone) support membranes. Three kinds of sulfonated poly(aryl ether sulfone)s with different amounts of phthalazinone moieties, namely, sulfonated poly(phthalazinone ether sulfone) (SPPES), sulfonated poly(phthalazinone biphenyl ether sulfone) (SPPBES), and sulfonated poly(phthalazinone hydroquinone ether sulfone)s (SPPHES), were used as coating materials. The solvents used in preparing the coating solution were investigated and optimized. The separation properties, thermal stability, and chlorine resistance of composite membranes were determined. The structures and morphologies of membranes were characterized with FTIR and SEM, respectively. The membrane prepared from SPPES with more phthalazinone moiety groups showed high water flux and salt rejection. The salt rejection of composite membranes followed the order SPPES > SPPHES > SPPBES. The rejection of the three composite membranes decreased slightly with the solution temperature rising from 20 to 90 degrees C, while the composite membrane with SPPES as the active layer showed a higher increase in flux than others. The results indicate that SPPES composite membranes show better thermal stability than others.