- Thermo- and mechanical-grinding-triggered color and luminescence switches of the diimine-platinum(II) complex with 4-bromo-2,2'-bipyridine
- 点击次数：
- 论文类型： 期刊论文
- 发表时间： 2014-01-07
- 发表刊物： DALTON TRANSACTIONS
- 收录刊物： EI、PubMed、SCIE、Scopus
- 卷号： 43
- 期号： 1
- 页面范围： 352-360
- ISSN号： 1477-9226
- 摘要： The square-planar diimine-platinum(II) complex, Pt(4-Brbpy)(C CC6H5)(2) (1) (4-Brbpy = 4-bromo-2,2'-bipyridine), was prepared and characterized. Solid-state 1 exhibits reversible thermo-and mechanical-grinding-triggered color and luminescence changes. When crystalline 1.2(CH2Cl2) or 1.2(CHCl3) are heated or ground, the original bright yellow-green emission centered at 525 (549, sh) nm changed to 637 and 690 nm, corresponding to thermo-and mechanochromic response shifts of approximately 88-112 nm and 141-165 nm, respectively. Meanwhile the crystalline state changes into an amorphous phase in both processes. Once the amorphous sample absorbs organic vapors, it can be reverted to the original crystalline state, along with red luminescence turning back to yellow-green emission. The reversibility of thermo-and mechanical-grinding-triggered chromic luminescence properties has been dynamically monitored by emission spectra and X-ray diffraction patterns. The dramatic thermo-and mechanical-grinding-triggered emission red shifts are most likely due to the conversion of the (MLCT)-M-3/(LLCT)-L-3 emission state into the (MMLCT)-M-3 triplet state.