论文类型：期刊论文

发表时间：2013-06-01

发表刊物：ACTA MATERIALIA

收录刊物：SCIE、EI

卷号：61

期号：11

页面范围：4289-4296

ISSN号：1359-6454

关键字：Nickel-based superalloy; gamma'-Phase precipitates; Electron microscopy

摘要：Rene 142, a commercial, columnar grained, gas turbine airfoil Ni-based superalloy, has been fabricated from a pre-alloyed, atomized powder by additive manufacturing using electron beam melting. Monolithic components having [001] oriented, columnar grain structures exhibited a creep-optimized 59% volume fraction of cuboidal, coherent, gamma'-phase precipitates averaging 275 nm on the side, and with y/y' channel widths ranging from 25 to 75 nm. Transmission electron microscopy, utilizing bright and dark field imaging of optimally oriented gamma/gamma' interfaces showed prominent misfit coherency strains as 5-fringe patterns. Corresponding hardness measurements also indicated the possibility of creep strength comparable with the commercial alloy. The notable feature of this study was the monolithic development of desirable superalloy properties without conventional, multi-step heat treatments. (C) 2013 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.