Controlled detonation synthesis of nano Fe-based oxides/SiO2 core-shell composite particles
点击次数：
论文类型：
期刊论文
发表刊物：
CHEMICAL PHYSICS LETTERS
收录刊物：
EI、SCIE
卷号：
740
ISSN号：
0009-2614
关键字：
Fe-based oxides/SiO2; Core-shell Structure; Controlled detonation;
Emulsion explosive
摘要：
Controlled detonation of emulsion Explosive and Hexogen (a kind of high explosive, for short, RDX) was performed to prepare Fe-based oxides/SiO2 nanoparticles. XRD (X-ray diffraction), TEM (Transmission electron microscope) and VSM (Vibrating sample magnetometer) experiments were performed to characterize and investigate the ingredients and phase structure of the granules, morphology, and distribution of the particles and the magnetism of the powders respectively. Results indicated that Fe/Urea complex detonation via emulsion explosives was advantageous to prepare Fe-based oxides/SiO2 core-shell powders, the inner FeO/Fe core was properly coated by a silica outer shell with the core size of around 50 nm and shell thickness of around 5-10 nm. And most of the raw detonation dust were converted into SiO2 coating Fe particles with the remained core-shell structure after proper thermal treatment. Raw powders obtained by RDX detonation presented weaker magnetism than that via emulsion explosives detonation, but which was substantially improved after thermal treatment.
发表时间：
2020-02-01
学位：博士
职称：研究员
学科：工程力学. 应用与实验力学. 生物与纳米力学
所在单位：力学与航空航天学院