标题：
Preparation and magnetic behavior of carbon-encapsulated iron nanoparticles by detonation method
点击次数：
论文类型：
期刊论文
发表刊物：
COMPOSITES SCIENCE AND TECHNOLOGY
收录刊物：
SCIE、EI、Scopus
卷号：
69
期号：
15-16
页面范围：
2554-2558
ISSN号：
0266-3538
关键字：
Nanoparticles; Detonation method; Carbon-encapsulated iron
nanoparticles; Magnetic properties
摘要：
Carbon-encapsulated iron (Fe@C) nanoparticles with core/shell structure have been successfully synthesized by detonation method, using a homemade composite explosive precursor. The detonation reaction was ignited by a non-electric detonator in nitrogen gas in an explosion vessel. The as-prepared detonation products were characterized by X-ray Diffraction, Transmission electron Microscopy, Raman spectroscopy and X-ray fluorescence. The magnetic behavior of the Fe@C materials was measured by vibrating sample magnetometer. The results showed that the detonation products were made up of the body centered cubic iron core and the graphitic carbon shell, of which the core diameter was in the range of 15-50 nm. Raman spectroscopy indicated that both graphitic and amorphous carbon occured in the outside shell structures. The hysteresis loops showed the as-made Fe@C nanoparticles were of superparamagnetic at 300 K temperature. A detonation reaction mechanism was proposed to explain the growth process of Fe@C nanoparticles based on these results. (C) 2009 Elsevier Ltd. All rights reserved.
发表时间：
2009-12-01
学位：博士
职称：研究员
学科：工程力学. 应用与实验力学. 生物与纳米力学
所在单位：力学与航空航天学院