发表刊物：JOURNAL OF MANUFACTURING PROCESSES

收录刊物：Scopus、SCIE、EI

卷号：30

页面范围：299-302

ISSN号：1526-6125

关键字：Mg/steel butt-welded plate; Nanoparticles; Fe-Ni solid solution; Interface; Welding

摘要：We created a Mg/steel butt-welded plate by hybrid laser-tungsten inert gas double-sided welding with a Ni interlayer. The tensile strength of the Mg/steel butt-welded plate reached 232 MPa, which was about 90.6% of the Mg alloy base metal (256 MPa). Uniform nanoparticles of the AlNi phase formed and then dispersed in the weld seam, which is conducive to improving its strength. The steel at the Mg/steel interface melted and formed an arc transition zone. The transition zone between the weld seam and the steel base metal was composed of a Mg/steel interface layer (1 mu m wide) and Fe-Ni solid solution (60-500 mu m wide), and we also found Al elements enriched in the Mg/steel interface. The addition of a Ni interlayer was found to significantly improve the weldability and also played a synergistic strengthening role on the weld seam and Mg/steel interface. (c) 2017 The Society of Manufacturing Engineers. Published by Elsevier Ltd. All rights reserved.