发表刊物：SURFACE & COATINGS TECHNOLOGY

收录刊物：SCIE、EI、Scopus

卷号：213

页面范围：139-144

ISSN号：0257-8972

关键字：Plasma nanotexturing; Polypropylene; Aging; Superhydrophobic state; Water adhesion; Surface restructuring

摘要：Polypropylene (PP) was modified by an oxygen capacitively coupled radio frequency plasma (CCP) under a radio frequency (RF) power of 200 W for an exposure time of 20 mm. The aging process of the plasma-modified PP was studied at temperatures of 20 degrees C, 60 degrees C, and 90 degrees C for 5 h. The post-aged PP surface with bundles of nanowires showed the as-modified surface morphology with a gradual decrease of the polar oxygen-containing groups. A hydrophobic over-recovery from the superhydrophilic state to the superhydrophobic state was observed on the post-aged PP surface. The as-modified superhydrophilic PP surface turned into the hydrophilic state at 20 degrees C and then the superhydrophobic state with the high water adhesion at 60 degrees C. The superhydrophobic state with the low water adhesion was achieved at 90 degrees C. Under the imposed pressure of 202 Pa to water droplet, the superhydrophobic surface with the high water adhesion shifted to the hydrophilic state and the superhydrophobic surface with the low water adhesion showed a good stability. The conversion from the superhydrophilic state to the superhydrophobic state on the post-aged PP surface by the plasma nanotexturing was ascribed to the change of the surface compositions under the acceleration of increased aging temperature. The change of contact geometry and the decrease of adhesive force of the liquid-solid interface in the TCL due to more intense surface restructuring under the stimulus of higher aging temperature aroused the transition of the water adhesion on the post-aged superhydrophobic PP surface by the plasma nanotexturing. (C) 2012 Elsevier B.V. All rights reserved.