A multi-component AlCrFe2Ni2 alloy with excellent mechanical properties
点击次数:
论文类型:期刊论文
发表时间:2016-04-15
发表刊物:MATERIALS LETTERS
收录刊物:SCIE、EI
卷号:169
页面范围:62-64
ISSN号:0167-577X
关键字:High entropy alloys; Alloy design; Microstructure; Mechanical properties
摘要:A cost effective Co-free AlCrFe2Ni2 high entropy alloy was designed and prepared based on reported AlCoCrFeNi2.1 eutectic high entropy alloys. The as-cast AlCrFe2Ni2 alloy showed a tensile yield strength of 796 MPa, an ultimate strength of 1437 MPa, and an elongation of 15.7%, which was superior to most high entropy alloys and was even comparable with the Ti-based ultrafine-grain alloy. The alloy consisted of noodle-like FCC phases, disordered BCC (A2) phases, and ordered BCC (B2) phases. The excellent mechanical properties of the alloy were attributed to the spinodal decomposition of BCC phases and the composite effect of the softer FCC and harder BCC phases. (C) 2016 Elsevier B.V. All rights reserved.