摘要：Cu-Ag-Zr alloy is a newly developed copper alloy material with an excellent combination of high mechanical strength and high electrical conductivity. Magnetic field was used in the solidification of Cu-Ag-Zr alloy. The results showed that with the application of magnetic field, formerly coarse columnar grain turned into homogeneous equiaxed grain. After aging, the precipitate of Zr had an increment and became more refined due to the reduction of segregation. The tensile strength and microhardness of Cu-0.1Ag-0.3Zr alloy under magnetic field of 15 mT increased by 17% and 10%, respectively. The electrical conductivity, with a slight decrease, was still as high as 92.4%IACS. ? (2015) Trans Tech Publications, Switzerland.