Synthesis and structure of [C6N4H20](0.5)[B5O6(OH)(4)]: A new organically templated pentaborate with white-light-emission

点击次数:

论文类型:期刊论文

第一作者:Yang, Yang

通讯作者:Meng, CG (reprint author), Dalian Univ Technol, Dept Chem, Dalian 116024, Peoples R China.

合写作者:Sun, Jiang-Bo,Cui, Miao,Liu, Rui-Bin,Wang, Yu,Meng, Chang-Gong

发表时间:2011-07-01

发表刊物:JOURNAL OF SOLID STATE CHEMISTRY

收录刊物:Scopus、SCIE、EI

卷号:184

期号:7

页面范围:1666-1670

ISSN号:0022-4596

关键字:Borate; Luminescence; White-light-emission

摘要:A new organically templated pentaborate [C6N4H20](0.5)[B5O6(OH)(4)] (la) was prepared by reactions of triethylenetetramine (TETA) with excess boric acid in aqueous solution and characterized by elemental analysis, FTIR, TG-DTA, powder X-ray diffraction and photoluminescence spectroscopy. The structure of la was determined by a single-crystal X-ray diffraction. It crystallizes in the monoclinic system with space group P2(1)/c, a=9200(3) angstrom, b=14.121(5) angstrom, c=10.330(4) angstrom, beta=91.512(4)degrees, V=1341.4(9) angstrom(3), and Z=4. The luminescent properties of the compound were studied, and a green-blue luminescence occurs with an emission maximum at 507 nm upon excitation at 430 nm. The photoluminescence of la can be modified from green-blue to white by means of a simple heat-treatment process. The white-light-emission of sample 1c makes the pentaborate a good candidate for display and lighting applications in the white LED. (C) 2011 Elsevier Inc. All rights reserved.