Facile Ammonia Synthesis from Electrocatalytic N-2 Reduction under Ambient Conditions on N-Doped Porous Carbon

点击次数:

论文类型:期刊论文

发表时间:2018-02-01

发表刊物:ACS CATALYSIS

收录刊物:ESI热点论文、SCIE、EI、ESI高被引论文

卷号:8

期号:2

页面范围:1186-1191

ISSN号:2155-5435

关键字:nitrogen fixation; ammonia synthesis; electrocatalysis; N-doped porous carbon; heterogeneous catalysis

摘要:Ammonia has been used in important areas such as agriculture and clean energy. Its synthesis from the electrochemical reduction of N-2 is an attractive alternative to the industrial method that requires high temperature and pressure. Currently, electrochemical N-2 fixation has suffered from slow kinetics due to the difficulty of N-2 adsorption and N  N cleavage. Here, N-doped porous carbon (NPC) is reported as a cost-effective electrocatalyst for ammonia synthesis from electrocatalytic N-2 reduction under ambient conditions, where its N content and species were tuned to enhance N-2 chemical adsorption and N  N cleavage. The resulting NPC was effective for fixing N-2 to ammonia with a high ammonia production rate (1.40 mmol g(-1) h(-1) at-0.9 V vs RHE). Experiments combined with density functional theory calculations revealed pyridinic and pyrrolic N were active sites for ammonia synthesis and their contents were crucial for promoting ammonia production on NPC. The energy-favorable pathway for ammonia synthesis was *N  N -> *NH=NH -> *NH2-NH2 -> 2NH(3).