点击次数：

论文类型：期刊论文

发表时间：2020-06-01

发表刊物：INTERNATIONAL JOURNAL OF FATIGUE

收录刊物：SCIE

卷号：135

ISSN号：0142-1123

关键字：VHCF; Fatigue strength; Threshold stress-defect size diagram; Stress intensity factor; GBF area

摘要：Unlike LCF (low cycle Fatigue) and HCF (high cycle fatigue), VHCF (very high cycle fatigue) failures of high-strength steel are mostly caused by internal nonmetallic inclusions. In view of fact that more than 90% of VHCF life is consumed in the process of crack propagation from inclusion to GBF (granular bright facet) boundary, the SIF (stress intensity factor) KGBF at the periphery of GBF could be regarded as a material constant independent of fatigue life, which could be also considered as the macro threshold SIF controlling the internal small-long crack growth. Therefore, based on experimental research and theoretical analysis, the threshold crack growth stress model was derived from the change of SIF considering the effect of local stress and crack configuration. This model diagramed the relationship between the threshold stress and defect size (including inclusions and cracks) and could be used for fatigue strength prediction. Finally, the validity of the threshold stress-defect size diagram was proved by the VHCF test data of other five kinds of high-strength steels.