点击次数：

论文类型：期刊论文

发表时间：2014-01-01

发表刊物：JOURNAL OF SOLID STATE ELECTROCHEMISTRY

收录刊物：SCIE、EI、Scopus

卷号：18

期号：1

页面范围：49-58

ISSN号：1432-8488

关键字：Activated nitrogen-doped carbon; Activation; Polyvinyl chloride; Electrochemical capacitor

摘要：Activated nitrogen-doped carbons (ANCs) were prepared by carbonization/activation approach using aminated polyvinyl chloride (PVC) as precursor. ANCs exhibit larger porosities and higher specific surface areas than those of their nitrogen-free counterparts for the same KOH/carbon ratio. The specific surface area of ANC-1 is up to 1,398 m(2) g(-1) even at a low KOH/carbon ratio of 1:1. Fourier transform infrared spectroscopy investigation of the nitrogen-enriched resin precursor indicates the efficient dehydrochlorination of PVC by ethylenediamine at a low temperature. The nitrogen content and the population of nitrogen functionalities strongly depend on the KOH/carbon ratios and decrease drastically after KOH activation as seen from the elemental and X-ray photoelectron spectroscopy analysis. The surface concentration of N-6 and N-Q almost disappears and the dominant nitrogen groups become N-5 after KOH activation. The highest specific capacitance of ANCs is up to 345 F g(-1) at a current density of 50 mA g(-1) in 6 M KOH electrolyte. ANCs also exhibit a good capacitive behavior at a high scan rate of 200 mV s(-1) and an excellent cyclability with a capacitance retention ratio as high as similar to 93 % at a current density of 2,000 mA g(-1) for 5,000 cycles.