点击次数：

论文类型：期刊论文

发表时间：2013-08-01

发表刊物：CARBON

收录刊物：SCIE、EI

卷号：59

页面范围：530-536

ISSN号：0008-6223

摘要：A carbon nanofiber (CNF)/carbon foam composite was fabricated from coal liquefaction residue (CLR) through a procedure involving template synthesis of carbon foam and catalytic chemical vapor deposition (CCVD) treatment. The high solubility and high pyrolysis yield make CLR a promising carbon precursor for the synthesis of carbon materials using the template method. The carbon foam has cell size of about 500 mu m and a porosity as high as 95 vol.%. Fe species naturally present in the CLR disperse homogeneously on the surface of the carbon foam acting as a catalyst in the CCVD process. After the CCVD treatment, the whole surface of the carbon foam is covered by entangled CNFs with external diameters of 20-100 nm and lengths of several tens of micrometers. The obtained CNF/carbon foam composites are effective selective adsorbents in the separation of oil and water, through a combination of hydrophobicity and capillary action. (C) 2013 Elsevier Ltd. All rights reserved.