点击次数：

论文类型：会议论文

发表时间：2018-01-01

收录刊物：CPCI-S、EI

卷号：424

期号：1

关键字：Cu-15Ni-8Sn; Vertical semi-continuous casting; Electromagnetic stirring; Microstructure evolution

摘要：In the present study, vertical semi-continuous casting equipped with the electromagnetic stirring (EMS) was applied in order to control the solidification process and obtain the anticipated homogeneous microstructure for Cu-15Ni-8Sn alloy. The experimental results indicate that the microstructure of as-cast Cu-15Ni-8Sn (wt.%) alloy prepared by conventional casting consists of Sn-depleted alpha phase (alpha Cu(Ni) solid solution), Sn-rich gamma phase ((CuxNi1-x)(3)Sn), and intermediate transition region (alpha+gamma), and most of the Sn element mainly segregates at dendritic grain boundary. Discriminatively, some equiaxed grains come into being in as-cast Cu-15Ni-8Sn alloy prepared by vertical semi-continuous casting, and Sn-rich gamma phases distribute on the matrix and grain boundary uniformly. Furthermore, the size of equiaxed grains becomes smaller after applying EMS, which reduces the segregation of Sn element to a large degree. In this study, microstructure evolution mechanism of Cu-15Ni-8Sn alloy prepared by conventional casting and by vertical semi-continuous casting without and with EMS is analyzed.