点击次数：

论文类型：期刊论文

发表时间：2020-05-20

发表刊物：COLLOIDS AND SURFACES A-PHYSICOCHEMICAL AND ENGINEERING ASPECTS

收录刊物：EI、SCIE

卷号：593

ISSN号：0927-7757

关键字：(NH4)(2)V6O16; Nanobelts; Hydrothermal synthesis; Zinc ion batteries; Long-term cycle

摘要：Aqueous rechargeable Zn-ion batteries (ARZIBs) have attracted great attention owing to many advantages including environmental protection, low cost and safety. Ammonium vanadates with multi-oxidation valence and open-framework layered structure, which is beneficial for zinc storage performance, are chosen as alternative candidates of cathode materials. (NH4)(2)V6O16 has received some attention in Li-ion battery, however, the electrochemical properties of (NH4)(2)V6O16 applied to ARZIBs has rarely reported comparatively. In this work, (NH4)(2)V6O16 nanobelts are prepared through a facile hydrothermal method and reported as the cathode material in ARZIBs. The Zn/(NH4)(2)V6O16 battery displays a wonderful rate capability with a staged reversible capacity of 322.0, 300.8, 267.5, 239.3, 209.2 mA h g(-1) at 0.1, 0.2, 0.5, 1, 2 A g(-1), respectively. The battery exhibits a high energy density (249 W h kg(-1)) and a long-term reversible cycling performance (78.3 % retained at 5 A g(-1) after 2000 cycles). The complete morphology of (NH4)(2)V6O16 after long-term cycle also illustrates its good flexibility during Zn2+ insertion/extraction without structural damage. Multiple analytical measurements methods are applied to investigate the major reaction mechanisms of the Zn2+ reversible (de)intercalation. The results demonstrate that the (NH4)(2)V6O16 as a cathode substitute is very promising for ARZIBs or other advanced battery systems.