Low-temperature synthesis of ZnTiO3 nanopowders
点击次数:
论文类型:期刊论文
发表时间:2009-01-15
发表刊物:4th Asian Conference on Crystal Growth and Crystal Technology
收录刊物:SCIE、EI、CPCI-S、Scopus
卷号:311
期号:3
页面范围:611-614
ISSN号:0022-0248
关键字:Crystallites; Zinc compounds; Dielectric materials
摘要:ZnTiO3 was successfully synthesized by a stearic acid gel method. The as-prepared nanopowders were characterized by X-ray diffraction (XRD), transmission electron microscope (TEM), scanning electron microscopy (SEM), Fourier transform infrared spectrometry, UV/vis diffuse reflectance spectra and thermal gravimetric analysis, respectively. The results show that the calcination process of stearic acid gel consists of a series of oxidation and combustion reactions in air, accompanied by exothermal effects. ZnO (zincite) was the dominant phase between 350 and 500 C. When the calcined temperature is higher than 500 C, ZnTiO3 can be formed and becomes the dominant phase at 600 C. SEM and TEM images of ZnTiO3 powders prepared at 600 C show that most ZnTiO3 nanopowders were agglomerated. The Fourier transform infrared spectra and UV/vis diffuse reflectance spectra can well confirm the observed XRD results. (C) 2008 Elsevier B.V. All rights reserved.