Superhydrophobic coatings on wood substrate for self-cleaning and EMI shielding
点击次数:
论文类型:期刊论文
第一作者:Xing, Yingjie
通讯作者:Song, JL (reprint author), Dalian Univ Technol, Minist Educ, Key Lab Precis & Nontradit Machining Technol, Dalian 116024, Peoples R China.
合写作者:Xue, Yaping,Song, Jinlong,Sun, Yankui,Huang, Liu,Liu, Xin,Sun, Jing
发表时间:2018-04-01
发表刊物:APPLIED SURFACE SCIENCE
收录刊物:SCIE、EI
卷号:436
页面范围:865-872
ISSN号:0169-4332
关键字:Superhydrophobic coating; Wood; Electromagnetic shielding; Self-leaning
摘要:A layer of superhydrophobic coating having good electromagnetic shielding and self-cleaning performance was fabricated on a wood surface through an electroless copper plated process. The superhydrophobic property of the wood surface was measured by contact angle (CA) and roll-off angle (RA) measurements. The microstructure and chemical composition of the superhydrophobic coating were analyzed by scanning electron microscopy (SEM), energy dispersive spectrometer (EDS) and X-ray diffraction (XRD). The analysis revealed that the microscale particles were uniformly distributed on the wood surface and the main component of the coating is metallic copper. The as-prepared Cu coatings on wood substrate exhibit a good superhydrophobicity with water contact angle about 160 degrees and rolling angle less than 5 degrees. (C) 2017 Elsevier B.V. All rights reserved.