采用移动式阴极制备大尺寸超亲水/超疏水铝板
点击次数:
发表时间:2012-01-01
发表刊物:机械工程材料
所属单位:机械工程学院
卷号:36
期号:4
页面范围:37
ISSN号:1000-3738
摘要:A large-area superhydrophilic/superhydrophobic aluminum plate was
prepared by moving-typed cathode based on the electrochemical machining
and fluoridation technology.The morphology and composition of the
aluminum plate surface were analyzed by scanning electron microscopy and
energy disperse spectroscopy,and the contact angle and roll angle were
measured by a contact angle meter,respectively.The results show that it
was feasible to prepare the large-area superhydrophilic/superhydrophobic
aluminum plate by the moving-typed cathode,and the superhydrophilic
aluminum plate surface with a binary micrometer-nanometer-scale rough
structure was found after electrochemical machining,and the contact
angle of the surface relative to water was 0°.This superhydrophilic
surface could be turned into the superhydrophobic surface with a water
contact angle of 167° and a roll angle less than 3° after fluoridation
treatment.