Regenerable CuO-Based Adsorbents for Low Temperature Desulfurization Application

点击次数:

论文类型:期刊论文

发表时间:2015-04-15

发表刊物:INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH

收录刊物:SCIE、EI、Scopus

卷号:54

期号:14

页面范围:3556-3562

ISSN号:0888-5885

摘要:A series of CuO-based adsorbents for deep removal of H2S at low temperature was prepared by a coprecipitation method. It was found that CuO-based adsorbents are able to remove H2S from a CO2 stream to less than 0.1 ppm at 40 degrees C. Among them, Fe-Cu-Al-O adsorbent exhibited the highest breakthrough capacity of 113.9 mg g(-1), which is more than 6 times that of pure CuO. The breakthrough capacity was also dependent on the adsorption temperature, space velocity, balance gas, and calcination temperature. The proper adsorption temperature should be lower than 100 degrees C in the presence of CO2, and a higher space velocity and calcination temperature could decrease the breakthrough capacity significantly. In addition, the CuO-based adsorbents had a regeneration rate of 43-90% in air at a relative low temperature from 100 to 200 degrees C with a stable breakthrough capacity after four adsorption-regeneration cycles.