点击次数:
论文类型: 期刊论文
发表时间: 2017-10-01
发表刊物: CORROSION SCIENCE
收录刊物: Scopus、SCIE、EI
卷号: 127
页面范围: 59-69
ISSN号: 0010-938X
关键字: Polymer; Ceramic; SEM; XPS; Oxidation; Polymer coatings
摘要: To improve the oxidation resistance of carbon fibers, a series of carborane-containing polymer-based coatings were prepared. The oxidation resistance and microstructure of the coatings were investigated. According to XPS, FT-IR and XRD analysis, the high oxidation resistance of the polymer-based coatings was attributed to the boron oxide protective layer formed from the oxidation of carborane groups in the coating. Ceramic coatings were prepared from heat treatment of polymer-based coatings under argon at 1300 degrees C for 2 h. The great oxidation resistance of the ceramic coating was attributed to the existence of boron carbide in coating.

蹇锡高

教授   博士生导师   硕士生导师

性别: 男

毕业院校:大连工学院

学位: 硕士

所在单位:化工学院

学科:高分子材料. 高分子化学与物理. 膜科学与技术

联系方式:手机:13904286124

电子邮箱:jian4616@dlut.edu.cn

邮箱 : jian4616@dlut.edu.cn

辽ICP备05001357号 地址:中国·辽宁省大连市甘井子区凌工路2号 邮编:116024
版权所有:大连理工大学
访问量: 手机版 English 大连理工大学 登录

开通时间:..

最后更新时间:..