Facile Preparation of Positively Charged and Solvent-Resistant Cellulose Acetate/LSCF Nanofiltration Membranes
点击次数:
论文类型: 期刊论文
发表时间: 2018-02-01
发表刊物: CHEMICAL ENGINEERING & TECHNOLOGY
收录刊物: SCIE、EI
卷号: 41
期号: 2,SI
页面范围: 313-318
ISSN号: 0930-7516
关键字: Cellulose acetate; Dye wastewater treatment; Nanofiltration; Nanofiltration membrane; Solvent resistance
摘要: Positively charged nanofiltration membranes often exhibit excellent antibacterial and antifouling properties. Nanofiltration membranes with high solvent resistance also find special applications in industrial waste water separation. Cellulose acetate is used to prepare various separation membranes due to its comprehensive performance. LSCF (La0.6Sr0.4Co0.2Fe0.8O3), a kind of cathode and electrolyte material, shows good conductivity in water solution. The nanosized hydrophilic inorganic additive LSCF is added to the casting solution to improve the performance of cellulose acetate nanofiltration membranes. After reaction with glutaraldehyde and trichloro dihydroxypropyl trimethylammonium chloride (TTAC), the prepared membrane demonstrates positively charged characteristics and excellent solvent resistance.

蹇锡高

教授   博士生导师   硕士生导师

性别: 男

毕业院校:大连工学院

学位: 硕士

所在单位:化工学院

学科:高分子材料. 高分子化学与物理. 膜科学与技术

联系方式:手机:13904286124

电子邮箱:jian4616@dlut.edu.cn

邮箱 : jian4616@dlut.edu.cn

辽ICP备05001357号 地址:中国·辽宁省大连市甘井子区凌工路2号 邮编:116024
版权所有:大连理工大学
访问量: 手机版 English 大连理工大学 登录

开通时间:..

最后更新时间:..