PPESK-Modified Multi-Functional Epoxy Resin and Its Application to the Pultrusion of Carbon Fiber
点击次数:
论文类型: 期刊论文
发表时间: 2018-10-01
发表刊物: POLYMERS
收录刊物: SCIE、PubMed、EI
卷号: 10
期号: 10
ISSN号: 2073-4360
关键字: carbon fiber; multi-functional epoxy resin; polyethersulfone resin; pultrusion process; curing
摘要: Multi-functional epoxy resins are generally brittle due to their high crosslinking densities, which can limit their use for applications that require impact resistance. Pultruded poly(phthalazinone ether sulfone ketone) (PPESK)-modified epoxy resins were prepared and their curing behaviors, heat resistance properties, and viscosity changes investigated. The glass transition temperature of these resins was found to increase with increasing PPESK content; however, these values were still compatible with the pultrusion process. Little change in the tensile strength and elongation lengths at breaking point were observed for blended PPESK/multi-functional epoxy resin containing 4-6% PPESK, and its viscosity levels were still within the requirements of the pultrusion process. Carbon fiber/multi-functional epoxy resin/PPESK (CF/E/PPESK) composites were also prepared and their performance investigated. The bending radius of these PPSEK-modified composites could reach up to 55 D with no cracking or peeling observed in their surface layers. The fatigue frequency of the sinusoidal waveforms for the composite did not change after one million fatigue test cycles, meaning that a strength retention rate of >90% was achieved. Therefore, this study describes a powerful approach for preparing toughened multi-functional epoxy resins that are well suited to pultrusion processes.

蹇锡高

教授   博士生导师   硕士生导师

性别: 男

毕业院校:大连工学院

学位: 硕士

所在单位:化工学院

学科:高分子材料. 高分子化学与物理. 膜科学与技术

联系方式:手机:13904286124

电子邮箱:jian4616@dlut.edu.cn

邮箱 : jian4616@dlut.edu.cn

辽ICP备05001357号 地址:中国·辽宁省大连市甘井子区凌工路2号 邮编:116024
版权所有:大连理工大学
访问量: 手机版 English 大连理工大学 登录

开通时间:..

最后更新时间:..