- SYNTHESIS AND CHARACTERIZATION OF POLY(PHTHALAZINONE BIPHENYL ETHER SULFONE KETONE)S FROM 4,4 '-DICHLOROBENZOPHENONE
- 点击次数：
- 论文类型： 期刊论文
- 发表时间： 2011-11-01
- 发表刊物： CHINESE JOURNAL OF POLYMER SCIENCE
- 收录刊物： Scopus、SCIE、ISTIC、CSCD
- 卷号： 29
- 期号： 6
- 页面范围： 719-725
- ISSN号： 0256-7679
- 关键字： Phthalazinone; Poly(aryl ether); Polycondensation; Processability; Thermal stability
- 摘要： A series of poly(aryl ether sulfone ketone)s containing phthalazinone and biphenyl moieties were synthesized by aromatic nucleophilic displacement polycondensation of 4-(4-hydroxylphenyl)(2H)-phthalazin-1-one (DHPZ), 4,4'-dichlorobenzophenone (DCB), 4,4'-dichlorodiphenyl sulfone (DCS) and 4,4'-biphenol (BP) in different molar ratios. The obtained copolymers were characterized by different instrumental techniques (FTIR, TGA, DSC, WAXD, etc.). The inherent viscosities of these polymers were in the range of 0.43-0.56 dL g(-1). They were amorphous and had good solubility in polar aprotic organic solvents. The copolymers exhibited high glass transition temperatures (T(g)s) between 225 degrees C and 256 degrees C and excellent thermal stability up to 517-526 degrees C (thermal decomposition temperatures for 5% weight loss, T(d), 5%) in nitrogen. The tensile strength and elongation at break of the polymers ranged from 63 MPa to 71 MPa and from 18% to 21%, respectively. The processability of the material was effectively improved by the introduction of biphenyl group into polymer backbone.