Thermal degradation kinetics of poly(aryl ether sulfone 1,3,5-triazine)s containing phthalazinone moieties
点击次数：
发布时间： 2019-03-09
发布时间：2019-03-09
论文类型：期刊论文
发表时间：2011-02-20
发表刊物：THERMOCHIMICA ACTA
收录刊物：EI、SCIE
卷号：514
期号：1-2
页面范围：51-57
ISSN号：0040-6031
关键字：1,3,5-Triazine; Poly(aryl ether sulfone); Heat resistance; Thermal analysis; Kinetics
摘要：Thermal degradation of phthalazinone-based poly(aryl ether sulfone 1,3,5-triazine) copolymers (PPESTs) has been investigated under nitrogen flow in dynamic heating conditions. Model-free kinetic approaches were applied to data for decomposition processes of PPESTs with different molecular structure. The activation energy was calculated as a function of the degradation extent by using Kissinger-Akahira-Sunose and Vyazovkin method. The effect of polymer composition and structure on the characteristic temperatures and kinetic parameters of thermal degradation was also investigated. The replacement of sulfone by 1,3,5-triazine in polymer main chain significantly increases initial decomposition temperature and Ea, and its stabilizing effect may be explained by the existence of two-stage decomposition process that suppresses unzipping of the copolymers. This assumption is supported by the experimental fact that the complete replacement of sulfone by 1,3,5-triazine increases the initial decomposition temperature by 31 degrees C and E, by at least 57 kJ/mol according to Vyazovkin method. (C) 2010 Elsevier B.V. All rights reserved.

蹇锡高

同专业博导 同专业硕导 个人学术主页

教授   博士生导师   硕士生导师

性别： 男

毕业院校：大连工学院

学位： 硕士

所在单位：化工学院

学科：高分子材料. 高分子化学与物理. 膜科学与技术

联系方式：

电子邮箱：

邮箱 :

辽ICP备05001357号 地址：中国·辽宁省大连市甘井子区凌工路2号 邮编：116024
版权所有：大连理工大学
访问量： 手机版 English 大连理工大学 登录

开通时间：..

最后更新时间：..