Synthesis and Properties of Soluble Copolyimides Containing Phthalazinone Moieties for Flexible Copper-clad Laminates
点击次数：
发布时间： 2019-03-09
发布时间：2019-03-09
论文类型：期刊论文
发表时间：2010-12-01
发表刊物：HIGH PERFORMANCE POLYMERS
收录刊物：Scopus、EI、SCIE
卷号：22
期号：8
页面范围：930-944
ISSN号：0954-0083
关键字：Copolyimide; phthalazinone; flexible copper-clad laminate
摘要：Soluble aromatic polyimides with good comprehensive properties are potential materials for microelectronics. A series of soluble copolyimides containing phthalazinone moieties were prepared from 1,2-dihydro-2-(4-aminophenyl)-4-[4-(4-(aminophenoxyl) phenyl)] (2H) phthalazin-1-one, 4,4'-diaminodiphenyl ether, as comonomers, and appropriate aromatic dianhydrides by one-pot solution polymerization in sulfolane. The corresponding copolyimide films had a good balance in thermal, adhesive and dielectric properties. The resulting copolyimides showed good solubility in polar aprotic solvents such as N-methyl-2-pyrrolidinone (NMP) and N, N-dimethyl acetamide and high thermal stability with glass transition temperatures in the range of 252-266 degrees C and decomposition temperature at 5% weight loss being above 505 degrees C in nitrogen. The copolyimide solutions in NMP were processed into flexible films which exhibited good adhesive property (1.66-2.28 N mm(-1)) and showed a predominantly amorphous nature measured by wide-angle X-ray diffraction. These free-standing films had dielectric constants of 2.3-3.1 (100 kHz) and low water absorption in the range of 0.76-0.93%. These outstanding properties make the obtained copolyimides good candidates for polyimide-based flexible copper-clad laminates.

蹇锡高

同专业博导 同专业硕导 个人学术主页

教授   博士生导师   硕士生导师

性别： 男

毕业院校：大连工学院

学位： 硕士

所在单位：化工学院

学科：高分子材料. 高分子化学与物理. 膜科学与技术

联系方式：

电子邮箱：

邮箱 :

辽ICP备05001357号 地址：中国·辽宁省大连市甘井子区凌工路2号 邮编：116024
版权所有：大连理工大学
访问量： 手机版 English 大连理工大学 登录

开通时间：..

最后更新时间：..