- Synthesis and properties of sulfonated poly(phthalazinone ether nitrile ketone)/boron phosphate composite membranes for PEMFC
- 点击次数：
- 论文类型： 期刊论文
- 发表时间： 2008-10-15
- 发表刊物： SOLID STATE IONICS
- 收录刊物： SCIE、EI、Scopus
- 卷号： 179
- 期号： 33-34
- 页面范围： 1940-1945
- ISSN号： 0167-2738
- 关键字： Sulfonated poly(phthalazinone ether nitrile ketone); Boron phosphate; Composite membrane; PEM; Proton conductivity
- 摘要： In this work, sulfonated poly(phthalazinone ether nitrile ketone)/boron phosphate (SPPENK/BPO(4)) composite membranes with BPO(4) content from 10 to 30 wt.% were prepared from SPPENK matrix, tripropylborate (C(3)H(7)O)(3)B and phosphoric acid (H(3)PO(4)) via an in situ process. The composite membranes were characterized using X-ray diffraction, FT-IR and TGA, which revealed the interaction between the sulfonic acid groups of SPPENK and BPO(4). The SPPENK/BPO(4) Composite membranes showed excellent thermal, oxidative and hydrolytic stabilities. The swelling ratios of composite membranes were about 5.0%, which was similar to that of SPPENK membrane. Proton conductivity of the composite membranes was studied under 100% relative humidity conditions up to 95 degrees C. A five-fold increase in proton conductivity was observed for the composite membrane with 30 wt.% BPO(4). (C) 2008 Elsevier B.V. All rights reserved.