- Influence of polymer structure on thermal stability of composite membranes
- 点击次数：
- 论文类型： 期刊论文
- 发表时间： 2005-07-01
- 发表刊物： JOURNAL OF MEMBRANE SCIENCE
- 收录刊物： SCIE、EI、Scopus
- 卷号： 256
- 期号： 1-2
- 页面范围： 116-121
- ISSN号： 0376-7388
- 关键字： thermal stability; reverse osmosis; composite membranes; interfacial polymerization; PPESK
- 摘要： Novel thermal stable polymer, poly (phthalazinone ether suffone ketone)s (PPESK), was used as the support material of the thin film composite (TFC) membranes fabricated via interfacial polymerization. Influence of polymer structure of both the support layer and the active layer on thermal stability of TFC membrane was studied, respectively. With the same fully aromatic polyarnide (PA) active layer, thermal stability of PA/PPESK TFC membrane is better than that of PA/PSE On the other hand, with the same PPESK support layer, thermal stability of TFC membranes with different active layer follows such sequence: fully aromatic > alicyclic aromatic > aliphatic aromatic. At 1.2 MPa pressure, 20 degrees C, fully aromatic PA/PPESK TFC membrane rejected 2000 ppm NaCl solution by 98% and water flux was 10.1 L/m(2) h. When solution temperature rose from 20 degrees C to 80 degrees C, water flux increased more than two-fold with stable salt rejection. Its permeation properties were almost unchanged from the original value after being operated at 90 degrees C for 8 h and then restarted at 20 degrees C. (c) 2005 Elsevier B.V. All rights reserved.