- Fluorinated phthalazinone-containing copolyimides for passive optical waveguides
- 点击次数：
- 论文类型： 期刊论文
- 发表时间： 2005-01-01
- 发表刊物： CHINESE JOURNAL OF POLYMER SCIENCE
- 收录刊物： Scopus、SCIE、EI、ISTIC
- 卷号： 23
- 期号： 1
- 页面范围： 71-74
- ISSN号： 0256-7679
- 关键字： polymeric optical waveguides; fluorinated polyimides; phthalazinone
- 摘要： A series of fluorinated copolyimides containing phthalazinone moieties were prepared from 2,2-bis(3,4dicarboxypheiiyl)hexafluoropropane dianhydride (6FDA), 3,3'4,4'-benzophenone-tetracarboxylic dianhydride (BPDA) and 2-(4-aminophenyl)-4-[4-(4-aminophenoxyl)phenyl]-2,3-phthalazin-1-one (DHPZ-2NH(2)) for making polymeric optical waveguides. The resulting copolymers containing 0-50 mol% BPDA/ DHPZ-2NH(2) show good solubility and are soluble in some organic polar aprotic solvents. The copolyimides also present excellent thermal stability. These polymers possess high glass transition temperature higher than 603 K and high decomposition temperature above 742 K determined by differential scanning calorimetry and thermogravimetric analysis, respectively, under a nitrogen atmosphere. Their refractive indices could be controlled by varying the ratio of 6FDA and BPDA in the copolymer from 0.5 to 1.0, and the in-plane refractive indices (n(TE)) range from 1.6366 to 1.6668 and the out-of-plane refractive indices (n(TM)) from 1.6024 to 1.6280 at 632.8 nm. The polymers birefringence (0.0342-0.0388) is almost independent of the 6FDA content of copolymer, which indicated that the phthalazinone-containing copolyimides could be suitable to fabricate optical waveguides possessing a low polarization dependent loss (PDL).