Key Words:Composite membrane; ATRP; TiO2; Antifouling; PVDF

Abstract:To improve PVDF (polyvinylidine fluoride) membrane property, TiO2 nano-particles can be blended in casting solutions to form composite membranes. In this study, TiO2 nano-particles were modified by coupling with gamma-aminopropyl triethoxy silane (KH550), then grafted with PMMA (Polymethyl methacrylate) or co-grafted with PMMA and more hydrophilic PSBMA (polysulfobetaine methacrylate) via ATRP (atom transfer radical polymerization). ATRP grafting time and weight ratio of KH550 to TiO2 were two main identified factors affecting TiO2 modification and membrane hydrophilicity, flux and antifouling properties. These were shown by Scanning electron microscopy (SEM) characterization, contact angles measurements and filtration tests with yeast suspensions. The grafted TiO2-PMMA nano particles formed after coupling at 3:1 weight ratio of KH550 to TiO2 and 5 h grafting, once composited with PVDF, formed a membrane with higher flux (up to 50%), higher flux recovery rate (FRR, 93.5%) and lower irreversible fouling (5.37%) than PVDF membrane composited with unmodified TiO2. Blending TiO2 co-grafted with PMMA and zwitterionic polymer PSBMA resulted in even better antifouling membranes (even lower R-ir < 2% and even higher FRR 99%). When the molar ratio of MMA to SBMA was 2 to 1, the highest steady flux and the highest FRR were obtained. (C) 2014 Elsevier B.V. All rights reserved.