发表刊物：DRYING TECHNOLOGY

收录刊物：SCIE、EI

卷号：27

期号：4

页面范围：523-528

ISSN号：0737-3937

关键字：Drying rate; Equilibrium moisture contents; Hydroscopicity; Magnesium hydroxide; Micro nanostructures; Moisture adsorption isotherm

摘要：Two kinds of Mg(OH)(2) nanosheets were prepared using a precipitation conversion method, and Mg(OH)(2) microparticles were synthesized by a direct precipitation method. Drying kinetics experiments of magnesium hydroxide of three morphological micro nanostructures were performed and their drying curves as well as drying rate curves were obtained at 80-140 degrees C. The equilibrium moisture adsorption isotherms of magnesium hydroxide of three morphological micro nanostructures at 12 degrees C were obtained. Results indicate that drying rate curves of magnesium hydroxide microparticles exhibit three stages: a setup period, a constant rate drying period, and a falling rate drying period. Drying rate curves of magnesium hydroxide nanosheets (nanosheets A and nanosheets B) show the same three stages with a small descending trend of constant rate drying period. It is also found that equilibrium moisture contents of Mg(OH)(2) nanosheets are larger than those of Mg(OH)(2) microparticles under the same drying conditions. The hydroscopicity of nanosheets A is the strongest and that of microparticles is the weakest.