点击次数：

论文类型：期刊论文

发表时间：2018-08-01

发表刊物：JOURNAL OF LASER APPLICATIONS

收录刊物：SCIE、CPCI-S

卷号：30

期号：3

ISSN号：1042-346X

关键字：pulsed laser processing; alumina ceramic sheet; morphology investigation; vapor-to-melt ratio; cutting quality

摘要：In order to reveal the relationship between vapor-to-melt ratio and processing quality in pulsed laser cutting of alumina ceramic sheets, experiments are carried out to obtain variations of the vapor-to-melt ratio with laser power, scanning speed, and thickness of ceramic sheet. By the morphological observation and analysis, the influence of the vapor-to-melt ratio on cutting quality is summarized. It is found that the vapor-to-melt ratio is increased with the increase of laser power, while it is decreased with the increase of scanning speed and the increase of sheet thickness. A good processing quality with suitable kerfs' width, better uniformity, and smaller roughness is obtained at a relatively large value of vapor-to-melt ratio. However, the excessive vapor-to-melt ratio will cause the deterioration of cutting stability and quality. Therefore, to meet the requirement, the vapor-to-melt ratio is controlled at around 0.1 to get 250 mu m of average kerfs' width and R-a less than 3.2 mu m of uniform kerfs. It reveals that the vapor-to-melt ratio is more intuitive to reflect the connection between the forms of material removal and cutting quality in laser processing, which provides an important theoretical and experimental support in the field of precision laser cutting on alumina ceramic sheets. (C) 2018 Laser Institute of America.