Deformation behavior of the oxide film on the surface of cold sprayed powder particle
点击次数：
论文类型：期刊论文
发表时间：2012-10-15
发表刊物：APPLIED SURFACE SCIENCE
收录刊物：SCIE、EI、Scopus
卷号：259
页面范围：294-300
ISSN号：0169-4332
关键字：Cold spraying (CS); Finite element analysis (FEA); Numerical simulation; Euler method; Oxide film; High velocity impact
摘要：In cold spraying, oxide-free interface is an important factor for metal-to-metal contact between powder particles and substrate, which determines the bonding strength and final coating quality. In this study, a systematic finite element analysis (FEA) is performed to examine the deformation behavior of the oxide film on an Al 6061-T6 particle surface after deposition. The simulation results show that the oxide film can be disrupted during the high velocity impact. Part of the cracked oxides remains at the interface and mainly accumulates at the central region after particle deposition. Substrate hardness, particle velocity and spray angle are found to influence the deformation behavior and final state of the oxide film. Besides, interparticle interaction is also investigated in the present work to clarify the deformation behavior of the oxide film inside the coating. (C) 2012 Elsevier B.V. All rights reserved.