点击次数：

论文类型：期刊论文

发表时间：2011-04-21

发表刊物：JOURNAL OF ALLOYS AND COMPOUNDS

收录刊物：SCIE、EI

卷号：509

期号：16

页面范围：5159-5162

ISSN号：0925-8388

关键字：Solid oxide fuel cell; Cathode-supported; Dry pressing; ScSZ

摘要：Cathode-supported solid oxide fuel cells (SOFCs), comprising porous (La0.75Sr0.25)(0.95)MnO3-delta (LSM) + Sm0.2Ce0.8O1.9 (SDC) composite cathode substrate and 11 mol%Sc2O3-doped ZrO2 (ScSZ) electrolyte membranes layer, were successfully fabricated via dual dry pressing method. NiO-SDC anode was prepared by slurry coating method. Phase characterizations and microstructures of electrolyte and cathode were studied by X-ray diffraction (XRD) and scanning electronic microscopy (SEM). No interface reaction took place between LSM/SDC cathode substrate and ScSZ electrolyte layer after sintered at 1300 degrees C. The cell performances were measured at 800 and 750 degrees C, respectively, by changing the external load. The peak power densities were 0.228 and 0.133 W cm(-2), and the corresponding open-circuit voltages of the cell were 1.092 and 1.027V at 800 and 750 degrees C, respectively. Impedance analysis indicated that the performances of the SOFCs were determined essentially by the composition and microstructure of the electrode. (C) 2011 Elsevier B.V. All rights reserved.