点击次数：

论文类型：期刊论文

发表时间：2009-01-15

发表刊物：5th International Conference on Physical and Numerical Simulation of Material Processing (ICPNS 07)

收录刊物：SCIE、EI、CPCI-S、Scopus

卷号：499

期号：1-2

页面范围：177-181

ISSN号：0921-5093

关键字：GCr15; Compression test; Dynamic recrystallization; Critical strain; Kinetic model

摘要：The dynamical recrystallization (DRX) of GCr15 steel was investigated at deformation temperatures of 950-1150 degrees C and strain rates of 0.1-10 s(-1) on a Gleeble-3800 thermo-mechanical simulator. The stress-strain curves at lower strain rates are typical of the occurrence of DRX and exhibit a peak in the flow stress before reaching steady state. The flow stress at higher strain rates increases rapidly to the maximum too, but followed by a steady region. The microstructures after deformation certify that DRX takes place in all specimens. And the results show that DRX occurs more easily with the decrease of strain rate and the increase of deformation temperature. Using regression analysis, the DRX activation energy of the steel, the relationship of critical strain and deformation conditions were determined. In order to determine the recrystallized fraction under different conditions, an approximate model based on the stress-strain curves was investigated, and the kinetic model for DRX was established. Crown Copyright (c) 2008 Published by Elsevier B.V. All rights reserved.