Constitutive Modeling of Dynamic Recrystallization Kinetics and Processing Maps of Solution and Aging FGH96 Superalloy
- 点击次数：
- 论文类型：期刊论文
- 发表时间：2013-12-01
- 发表刊物：JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
- 收录刊物：SCIE、EI、Scopus
- 文献类型：J
- 卷号：22
- 期号：12
- 页面范围：3728-3734
- ISSN号：1059-9495
- 关键字：dynamic recrystallization; FGH96 superalloy; hot deformation; processing
maps
- 摘要：The hot deformation behavior of solution and aging FGH96 superalloy were investigated in the deformation temperature range of 1000-1175 degrees C and strain rate range of 0.001-5.0/s on a Gleeble-1500 thermo-mechanical simulator. The results show that the true stress-strain curves are typical of the occurrence of dynamic recrystallization (DRX). The value of the activation energy and materials constants of A and n was obtained through the hyperbolic sine function between the peak stress and Zener-Hollomon parameter. Optical microscopy observations of the grains showed that Zener-Hollomon parameter affected the DRX grain size obviously. In addition, the constitutive equations and DRX kinetics model were also built. The processing maps with the strain of 0.3 and 0.6 were obtained on the basis of dynamic materials model. The results predicted that there existed instability regions at around 1050 degrees C when the strain rate exceeds 0.01/s.