点击次数：

论文类型：期刊论文

发表时间：2013-02-01

发表刊物：JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION

收录刊物：ISTIC、SCIE、EI

卷号：28

期号：1

页面范围：82-87

ISSN号：1000-2413

关键字：carbon nanotubes; Portland cement; dispersibility; reinforcement; morphological properties

摘要：Stable homogeneous suspensions of multi-walled carbon nanotubes (MWCNTs) were prepared using gum arabic (GA) as dispersant and were incorporated to Portland cement paste. The dispersion was examined by ultraviolet visible spectroscopy (UV-vis), and the concentration measurement shows that the optimum concentration of GA is 0.45 g center dot L-1. The dispersibility of the surface-modified MWCNTs in aqueous solution and cement matrix were investigated by transmission electron microscopy (TEM) and energy dispersive spectroscopy (EDS), and the mechanical properties of the composites were investigated. The results show that the addition of the treated nanotubes can improve both the flexural strength and the compressive strength of the Portland cement composite significantly. The flexural strength of the composite increases up to 43.38% with the MWCNT concentration of 0.08% (by weight of cement). The porosity and pore size distribution of the composites were measured by mercury intrusion porosimetry (MIP), and the results indicate that the cement paste doped with MWCNTs obtained lower porosity and concentrated pore size distribution. The morphological structure was analyzed by field emission scanning electron microscopy (FESEM) and EDS. It is shown that MWCNTs act as bridges and networks across cracks and voids, which transfer the load in case of tension, and the interface bond strength between the nanotubes and matrix is very strong.