发表刊物：CHINA FOUNDRY

收录刊物：SCIE、Scopus

卷号：6

期号：3

页面范围：214-218

ISSN号：1672-6421

关键字：grain size; nucleation and growth; microstructure

摘要：The optical microscopy and scanning electron microscopy as well as energy dispersive spectroscopy were employed to investigate the influence of joint addition of Sc and Zr on grain refinement of Al-Zn-Mg-Cu alloys. Results show that the addition of 0.20% Sc has a little effect on grain refinement because Sc is mainly dissolved into the matrix and hardly any primary Al(3)Sc particles are precipitated. The alloy with addition of 0.30% Sc and 0.16% Zr has more equiaxed grains than that of others, giving cast grain sizes as. ne as 13 mu m. This is because the Sc substitutes for Al atom in the Al-Zr crystal cell and forms Al-Sc-Zr unit cell, which grows and becomes Al(3)(Sc(x),Zr(1-x)) particle, acting as a nucleus for the formation of alpha-Al. The addition of 0.04% Ti and 0.008% B makes the grain size drop from 250 mu m to 50 mu m. Its refinement effect is less than the 13 mu m achieved by the alloy including 0.30% Sc and 0.16% Zr.