Mg(OH)(2) crystals synthesized by CHM method

Hits:

Indexed by:会议论文

Date of Publication:2010-09-25

Included Journals:EI、CPCI-S、Scopus

Volume:688

Page Number:153-+

Key Words:Mg(OH)(2); CHM; Hexagonal plates; cubic crystals; SEM; XRD

Abstract:Using Mg(NO3)(2)center dot 6H(2)O as raw materials, Mg(OH)2 crystals were synthesized by a composite-hydroxide-mediated(CHM) method at 160-200 degrees C for 24 h. Hexagonal plates Mg(OH)2 crystal were formed at high content of magnesium nitrate. The size of the plates increased to 5-15 mu m while the content of magnesium nitrate was 30 mmol. The strength of (001) plane became stronger than (101) plane with the high content of magnesium nitrate, and this tendency became more obvious at high magnesium nitrate concentration. It is explained that the more Mg2+ ion fill the polar plane. The strength of (001) plane became stronger than (101) plane at high temperature. It can be explained Mg(OH)(2) crystal become more steady with more non-polar plane at high temperature, and the shape of the sample showed a change from irregular to cubic shape with heated temperature increase. It indicates that the Mg(OH)(2) crystal growth benefits from high temperature. It is conjectured that the connecting of the [Mg(OH)(6)](4+) basic units with the common edges change into common vertex angle.

Pre One:基于RBF神经网络模型的臭氧浓度软测量研究

Next One:Transient 3D simulation of a submerged-arc furnace for production of MgO single crystal