Hits:

Indexed by:期刊论文

Date of Publication:2014-02-01

Journal:PROGRESS IN NATURAL SCIENCE-MATERIALS INTERNATIONAL

Included Journals:SCIE、CSCD

Volume:24

Issue:1

Page Number:35-41

ISSN No.:1002-0071

Key Words:Maraging stainless steels; Composition design; Cluster structure model; Super-high strength

Abstract:The composition characteristics of maraging stainless steels were studied in the present work investigation using a cluster-plus-glue-atom model. The least solubility limit of high-temperature austenite to form martensite in basic Fe-Ni-Cr corresponds to the cluster formula [NiFe12]Cr-3, where NiFe12 is a cuboctahedron centered by Ni and surrounded by 12 Fe atoms in FCC structure and Cr serves as glue atoms. A cluster formula [NiFe12](Cr2Ni) with surplus Ni was then determined to ensure the second phase (Ni3M) precipitation, based on which new multi-component alloys [(Ni,Cu)(16)Fe-192](Cr-32(Ni,Mo,Ti,Nb,Al,V)(16)) were designed. These alloys were prepared by copper mould suction casting method, then solid-solution treated at 1273 K for 1 h followed by water-quenching, and finally aged at 783 K for 3 h. The experimental results showed that the multi-element alloying results in Ni3M precipitation on the martensite, which enhances the strengths of alloys sharply after ageing treatment. Among them, the aged [(Cu4Ni12)Fe-192](Cr-32(Ni8.5Mo2Ti2Nb0.5Al1V1)) alloy (Fe74.91Ni8.82Cr11.62Mo1.34Ti0.67Nb0.32Al0.19V0.36Cu1.78 wt%) has higher tensile strengths with YS = 1456 MPa and UTS = 1494 MPa. It also exhibits good corrosion-resistance in 3.5 wt% NaCl solution. (C) 2014 Chinese Materials Research Society. Production and hosting by Elsevier B.V. All rights reserved.