长期从事金属材料蠕变、组织演化、损伤及寿命预测工作。主持和参加国家自然科学基金重点和面上项目6项,“863”计划课题2项,省部级及企业项目20余项。获国家发明专利5项,发表学术论文200余篇。出版专著“耐热钢持久性能的统计分析及可靠性预测”1部(科学出版社),译著“高温合金”1部,编著1部。获辽宁省教学名师,宝钢教育奖优秀教师奖。辽宁省教学成果一等奖1项,国家本科一流课程、国家精品在线开放课程负责人。Emerald出版社颁发的学术奖“Literati Club Awards for Excellence”,金属学报2009-2015年度优秀论文奖。省部级科技奖励一等奖、二等奖5项。

论文成果
当前位置 : 中文主页 >> 科学研究 >> 论文成果

Microstructure evolution and mechanical properties degradation of HPNb alloy after a five-year service

点击次数:


论文类型:期刊论文

发表时间:2018-04-01

发表刊物:MATERIALS RESEARCH EXPRESS

收录刊物:SCIE

卷号:5

期号:4

ISSN号:2053-1591

关键字:microstructure evolution; degradation; HPNb alloy; carbide; creep strength

摘要:The microstructure and mechanical properties of ethylene cracking furnace tube (HPNb alloy) are investigated by scanning electronic microscopy (SEM), tensile tests and Charpy impact tests at room temperature, tensile tests and creep tests at high temperature in this paper. The primary carbides of HPNb alloy coarsened and formed a continuous network after a five-year service. Furthermore, a lot of fine secondary carbides precipitated in the dendrite interior. The primary carbides M7C3 and NbC transformed into M23C6 and G phase after service, respectively. The furnace tube after service exhibits higher yield strength, lower tensile strength, worse ductility and toughness than as-cast tube at room temperature. At high temperature, the tensile strength and yield strength of service tube are higher than as-cast tube, but its tensile elongation is lower. The creep strength of HPNb alloy at high temperature decreases after a five-year service. Both microstructure and mechanical properties of ethylene cracking furnace tube have deteriorated after a five-year service.

发表时间:2018-04-01

上一条: Influence of specimen thickness on the creep behavior of a directional solidification nickel-based sulperalloy

下一条: Effect of Surface Fe-Sn Intermetallics on Oxide Films Formation of Stainless Steel in High Temperature Water