Microstructure, mechanical properties and springback behaviour of Ti-6Al-4V alloy connection rod for spinal fixation device

点击次数:


论文类型:期刊论文

发表时间:2019-01-01

发表刊物:MATERIALS SCIENCE & ENGINEERING C-MATERIALS FOR BIOLOGICAL APPLICATIONS

收录刊物:SCIE、PubMed、Scopus

卷号:94

页面范围:811-820

ISSN号:0928-4931

关键字:Titanium alloy; Connection rod of spinal fixation device; Strength; Modulus; Springback behaviour

摘要:The effect of annealing condition on microstructure, mechanical properties and springback behaviour was examined in the connection rod of Ti-6Al-4V alloy for spinal fixation devices. Compared with the deformed microstructure in the sample before annealing, relatively few equiaxed grains were present after annealing at 1003 K after 1.8 ks, and a considerable amount appeared at 7.2 ks. When annealing time was extended to 36 ks, the recrystallised grains further grew. Vickers hardness, tensile strength and bending strength decreased with increasing annealing time, whereas the elastic and bending moduli showed no significant change with annealing time of up to 7.2 ks and then slightly decreased at 36 ks. The springback ratio was closely associated with strength and modulus and applied bending deflection. The springback ratio reached the highest and lowest values in the sample before and after annealing for 7.2 ks, respectively. A good combination of strength, modulus and springback ratio was obtained in the sample after annealing for 7.2 ks.

发表时间:2019-01-01

上一条: First-principles study of phase stability and elastic properties in metastable Ti-Mo alloys with cluster structure

下一条: Interaction Mechanism between Zn and Passivated Stainless Steel


手机版

同专业博导  同专业硕导  个人学术主页

欢迎您访问我们的网站,您是第 位访客

辽ICP备05001357号 地址:中国·辽宁省大连市甘井子区凌工路2号 邮编:116024
版权所有:大连理工大学

最后更新时间:..
开通时间:..