点击次数：

论文类型：期刊论文

发表时间：2017-12-01

发表刊物：FRONTIERS OF ENVIRONMENTAL SCIENCE & ENGINEERING

收录刊物：Scopus、SCIE、EI

卷号：11

期号：6

ISSN号：2095-2201

关键字：Si; alpha-Fe2O3; Photoelectrochemistry; Photogenerated charge separation

摘要：The spontaneous oxidation process of pristine silicon (Si) limits its application as photocatalyst or electrode in aqueous solution or moist air. Covering a protection layer on Si surface is an effective approach to overcome this disadvantage. In this paper, alpha-Fe2O3 is demonstrated to be an excellent alternative as a protection material. alpha-Fe2O3 layer was deposited around each p-type Si micropillar (SiMP) in well-ordered array by chemical bath deposition method. The diameter of SiMP was 5 mm and the thickness of alpha-Fe2O3 layer was about 20 nm. The photoeletrochemical stability of SiMP/alpha-Fe2O3 was proved by 10 circles cyclic voltammetry testing. Compared with SiMP, its optical absorption and photocurrent density improved 2 times and 4 times, respectively, and its onset potential for hydrogen evolution moved positively about 0.4 V. These improved performances could be ascribed to the enhanced photogenerated-charge-separation efficiency deriving from built-in electric field at the interface between Si and alpha-Fe2O3. The above results show an effective strategy to utilize Si material as photocatalyst or electrode in aqueous solution or moist air. (C) Higher Education Press and Springer-Verlag Berlin Heidelberg 2017