论文类型：期刊论文

发表时间：2016-01-01

发表刊物：SENSORS AND ACTUATORS B-CHEMICAL

收录刊物：SCIE、EI

卷号：222

页面范围：1134-1143

ISSN号：0925-4005

关键字：Gas sensor; SnO2; Biotemplate; Formaldehyde

摘要：A biotemplate of grapefruit exocarp was used to synthesis porous hierarchical SnO2 and its gas sensing properties were investigated in this manuscript. Biomorphic SnO2 with lamellar and plicated membranes and porous walls were synthesized by using grapefruit exocarp template combining with ultrasonic shaking and following calcination. The porous hierarchical structure of biomorphic SnO2 was characterized by field emission scanning electron microscope, transmission electron microscopy, nitrogen adsorption-desorption isotherm, etc. The biomorphic SnO2 exhibits small grain size around 10 nm, a relatively large BET surface area and mesoporosity. Growth mechanism of biomorphic SnO2 was proposed. The sensing properties of the biomorphic SnO2 to formaldehyde vapor were measured. The optimal operating temperature of the sensor was 200 degrees C and the response value of the sensor to 10 ppm formaldehyde was 50. The sensor showed a good selectivity to formaldehyde in methanol, acetone, toluene, benzene and ammonia. The stability and the effect of humidity of the sensor were also tested. The gas sensing mechanism of the biomorphic SnO2 to formaldehyde was analyzed briefly. (C) 2015 Elsevier B.V. All rights reserved.