Branched phenyl-s-triazine moieties to enhance thermal properties of phthalonitrile thermosets

点击次数:

论文类型:期刊论文

发表时间:2018-02-01

发表刊物:POLYMER INTERNATIONAL

收录刊物:SCIE、EI

卷号:67

期号:2

页面范围:189-196

ISSN号:0959-8103

关键字:phthalonitrile resins; branched; phenyl-s-triazine; thermal stability

摘要:Heat-resistant materials have made tremendous progress in marine, aerospace and microelectronic fields. Herein, a new class of phthalonitrile resins, branched poly(biphenyl ether triphenyl-s-triazine) phthalonitriles, were successfully synthesized via a two-step, one-pot reaction, on the basis of 2,4,6-tris(4-fluorophenyl)-1,3,5-triazine and 4,4-biphenol. 4,4-Diaminodiphenylsulfone was employed to facilitate the curing reaction, and successful realization of curing behavior was concluded from rheological and differential scanning calorimetric studies, indicating the obtained resins possess favorable processability. The relationship between concentration of reactants and properties of the resins was systematically studied. After thermal curing, the E-glass fiber-reinforced composite, prepared with a concentration of reactants of 0.15 g mL(-1), shows an admirable glass transition temperature of 480 degrees C and commendable thermal stability with 5% weight loss temperature in nitrogen of 563 degrees C, suggesting that the improvement of the thermal properties stems from the branched structure and the phenyl-s-triazine units. (c) 2017 Society of Chemical Industry