发表刊物：MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING

收录刊物：SCIE、EI

卷号：691

页面范围：81-87

ISSN号：0921-5093

关键字：Magnesium alloys; Large strain hot rolling; Warm rolling; Grain refinement; Mechanical properties

摘要：A simple process named two - stage rolling was proposed and investigated to obtain a fine-grained microstructure of AZ31 Mg alloy sheet. The first stage rolling is deformed at 773 K with a large reduction by single pass, while the second stage process is a multi-pass warm rolling deformed at 573 K. Microstructure and texture were measured on sheets subjected to rolling experiments of different reductions, and the tensile test was also carried out. After the two-stage rolling and subsequent annealing, reductions as large as 89% were achieved without surface cracking; the AZ31 alloy sheet exhibits a homogenous microstructure with fine grains and weak basal texture, where the final average grain size is stabilized around 3 pm; thus, it shows the high strengths and good ductility.