点击次数：

论文类型：期刊论文

发表时间：2008-04-01

发表刊物：MATERIALS CHARACTERIZATION

收录刊物：SCIE、EI

卷号：59

期号：4

页面范围：402-406

ISSN号：1044-5803

关键字：nitinol; stent; superelasticity; shape-setting treatment; phase transformation temperature

摘要：Ageing treatments were performed on Ti-50.7 at.% Ni (nitinol) stent wires. The results of shape-setting, austenite finish temperature and the non-linear mechanical properties of nitinol stent wires at body temperature were investigated. The experimental results show that the shape-setting results were stable when wires were constrain-treated at 500 and 550 degrees C and the ageing time was longer than 10 min. Austenite finish temperatures of the wires increased with ageing time, and decreased with ageing temperature after an initial increase. The peak value of the transition temperature was found to be 400 degrees C. For the same ageing temperature, both the upper and lower plateau stresses decreased slightly with ageing time. Most of the treated nitinol wires retained good recovery ability at body temperature; permanent sets were less than 0.05% when the ageing treatment was performed at 500 degrees C for not more than 60 min. (c) 2007 Elsevier Inc. All rights reserved.