Indexed by:期刊论文

Date of Publication:2018-01-01

Journal:HIGH PRESSURE RESEARCH

Included Journals:SCIE、EI

Volume:38

Issue:1

Page Number:41-52

ISSN No.:0895-7959

Key Words:Tungsten-copper composite; underwater explosive compaction-sintering; bonding strength; copper matrix composite

Abstract:This study investigated underwater explosive compaction-sintering for coating a high-density tungsten-copper composite on a copper surface. First, 50% W-50% Cu tungsten-copper composite powder was prepared by mechanical alloying. The composite powder was pre-compacted and sintered by hydrogen. Underwater explosive compaction was carried out. Finally, a high-density tungsten-copper coating was obtained by diffusion sintering of the specimen after explosive compaction. A simulation of the underwater explosive compaction process showed that the peak value of the pressure in the coating was between 3.0 and 4.8 GPa. The hardness values of the tungsten-copper layer and the copper substrate were in the range of 87-133 and 49 HV, respectively. The bonding strength between the coating and the substrate was approximately 100-105 MPa.