点击次数：

论文类型：期刊论文

发表时间：2016-12-20

发表刊物：ELECTROCHIMICA ACTA

收录刊物：SCIE、EI、Scopus

卷号：222

页面范围：446-454

ISSN号：0013-4686

关键字：carbon fibres; supercapacitor; nickel tungsten tetraoxide

摘要：A novel NiWO4/Ni/carbon fibre composite was fabricated by the combination of electrospining with spray deposition and subsequent carbonization. It was revealed that NiWO4 and Ni were uniformly dispersed outside and inside the carbon fibres, respectively. Used as supercapacitor electrode, the as prepared fibre composite shows excellent capacity and cyclability. Galvanostatic discharge/charge test showed that the specific capacitance sharply increased from 151.1 to 792.2Fg(-1) at 5 Ag-1 after 1500 cycles, which was attributed to the oxidation of metallic Ni into ionic Ni2+ forming more reactive sites. An electrochemical asymmetric supercapacitor was assembled using the composite fibres and porous carbon nanofibers, of which the energy density increased from 32.5 to 41.3 Wh kg(-1) at 193.8 W kg(-1). The results clearly showed that NiWO4/Ni/carbon fibre material is of potential in energy harvesting and storage. (C) 2016 Elsevier Ltd. All rights reserved.