点击次数：

论文类型：会议论文

发表时间：2011-11-04

收录刊物：EI、CPCI-S、Scopus

卷号：512-515

页面范围：407-+

关键字：Oxide ceramic composite; Superplastic forming; Mechanical properties

摘要：The paper mainly focused on the two issues that restricted the practical application of superplastic ceramics, which were the low strain rate in superplastic forming as well as resulted severely cavitation in deformed materials. The alumina-based composites Al2O3-ZrO2(3Y) and Al2O3-30mol%ZrO2(3Y)-30mol%MgAl2O4 (AZ30S30) were selected as research materials. The nano-sized composite powders were synthesized by heating of ethanol-aqueous salt solution method. The superplastic forming tests under the compressive stress state were carried out to evaluate the superplastic formability of the as-sintered materials. The results demonstrated that the following conditions were the essentials for attaining high-strain-rate superplastic forming in alumina based ceramic composites: reduced the initial grain size and suppressed dynamic grain growth in deformation by second phase dispersion, enhanced diffusivity by co-doped certain elements, as well as provided new rate-controlling accommodation process in superplastic forming. The results also indicated that during the superplastic forming the cavitation damage was eliminated because of the compression stress state, which ensured the mechanical properties after deformation.